DIN 1.5918 17crni6-6 Engineering Steel Bar with Good Quality

Model NO.
DIN1.5918 17CrNi6-6
Composition
Ferrous Steel Scrap
Technique
Forged Rolled
Shape
Round Flat
Surface Treatment
Black, Grinded, Peeled, Rough Turned, Polished
Special Use
Mold Steel
Application
Structural Steel Bar
Size Range
20-480 mm
Quality Standard
BS En ISO 4957
Steel-Making Condition
Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+E
MOQ
1t
Transport Package
Seaworthy Packing
Specification
DIN1.5918 17CrNi6-6
Trademark
FUSHUN
Origin
, China
HS Code
7228600000
Production Capacity
500tons Per Month
Reference Price
$ 540.00 - 3,600.00
Contact Us

Product Description

DIN1.5918 17CrNi6-6 Engineering Steel

Similar Grade: DIN1.5918 17CrNi6-6

Shape: Round, Flat, Square.

Size Range:
  Diameter(mm) Thickness (mm) Width (mm) Length(mm)
Round 20-420 - - 2000-5800
Square 20-420 - - 2000-5800
flat - 20-50 50-600 2000-5800
 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR

Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:

2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 
Packing details In seaworthy packing, as your requirement.
Delivery details within 30-50 days
 
Chemical Composition:
Grade C Mn P S Si Cr Ni
1.5918 0.14-
0.20 		0.50-
0.80 		0.025
max 		0.035
max 		0.40
max 		1.40-
1.70 		1.40-
1.70



 
 
 

Mechanical Properties:

Process 		Diameter(mm) Tensile Strength Rm (Mpa) Hardness (HB)
Treated to improve shearability / / 255 max
SOFT ANNEALED / / 229 max
Treated for strength / / 175-229
Treated for ferrite and pearlite structure and hardness range / / 156-207
QUENCHED AND TEMPERED 16 max 1200 min /
QUENCHED AND TEMPERED 16-40 1100 min /
QUENCHED AND TEMPERED 40-100 900 min /

 
Heat Treatment and Fabrication:

 
 
 
 
 
 
Process Temperature(oC) Media
Forging or hot rolling 1100-850 /
Normalising 850-880 air
Soft annealing 650-700 furnace
Carburising 880-980 /
Core hardening 830-870 oil
Intermediate annealing 630-650 /
Case hardening 780-820 oil
Tempering 150-200 /
 

Applications:
Alloyed case hardening steel for highly strained parts and good toughness at core tensile strength of 900 - 1200 N/mm². Driving bevel gears, crown wheels, gears, shafts, bolts for automotive and gear components.
Introduction:
Structural, pressure vessel and engineering steels.
 