DIN1.5752 15nicr13 Flat Structural Alloy Steel

Model NO.
DIN1.5752 15NiCr13
Composition
Ferrous Steel Scrap
Technique
Forged, Rolled
Shape
Round, Flat, Square.
Surface Treatment
Black, Grinded, Peeled, Rough Turned, Polished
Special Use
Silicon Steel
Application
Flange Plate
Size Range
20-420mm
Similar Grades
DIN1.5752 15nicr13
Steel-Making Condition
Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+E
Delivery Condition
Annealed, Quenched + Tempered
Transport Package
Seaworthy Packing
Specification
DIN1.5752 15NiCr13
Trademark
FUSHUN
Origin
Huangshi, China
HS Code
7228600000
Production Capacity
500tons Per Month
Reference Price
$ 900.00 - 3,600.00
Contact Us

Product Description

DIN1.5752 AMS6260E 655H13 15NiCr13 Case Hardening Steel
Similar Grade: DIN1.5752 AMS6260E 655H13 15NiCr13 
Shape: Round, Flat, Square.
Size Range:
  Diameter(mm) Thickness (mm) Width (mm) Length(mm)
Round 20-420 - - 2000-5800
Square 20-420 - - 2000-5800
flat - 20-50 50-600 2000-5800
 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:

2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 
Packing details In seaworthy packing, as your requirement.
Delivery details within 30-50 days
 
Chemical Composition:
Grade C Mn P S Si Cr Ni
1.5752 0.14-
0.20 		0.40-
0.70 		0.025
max 		0.035
max 		0.40
max 		0.60-
0.90 		3.00-
3.50



 
 
 

Mechanical Properties(T=20°C if not differently stated)

Process 		Diameter(mm) Tensile Strength Rm (Mpa) Yield Strength Rp0.2 (Mpa) Elongation A5 (%) Area Reduction Ratio C (%) Hardness (HB)
Soft Annealing / / / / / 255 max
Treated to hardness range / / / / / 179-229
Treated to ferrite-pearlite structure / / / / 166-217  
Quenched and tempered 11 max 1030-1320 835 min 9 min 40 min /
Quenched and tempered 11-30 930-1230 785 min 10 min 45 min /
Quenched and tempered 30-63 880-1180 735 min 10 min 45 min /
 
 
 
 
Heat Treatment and Fabrication:
 
Process Temperature(ºC)
End quench test Austenitizing 880 min
Carburizing 880-980
Core-hardening 840-880
Case-hardening 780-820
Tempering 150-200
 
 

Product Introduction:
Good machinability (hobbing and turning).
Good dimensional stability.
Homogenous PESR structure suitable for the production of large components.
Improved polishability, photo-etchability and EDM due to higher purity.
Suitable for single and double hardening.
 
 