Cold Work 1.2063 Steel (DIN1.2063)

Model NO.
1.2063
Composition
Ferrous Steel Scrap
Technique
Forged
Shape
Round Bar, Square Bar, Flat Bar
Surface Treatment
Grinded, Peeled (Centreless Turned)
Special Use
Mold Steel
Application
Tool Steel Bar
Size
Hot Rolled 12mm-120mm, Hot Forged Round
Delivery Conditions
Annealed, Qunched and Tempered
Surface Condition
Black Surface, Grinded, Peeled
Quality Standard
BS En ISO 4957
Transport Package
Seaworthy Packing
Specification
1.2063
Trademark
FUSHUN
Origin
Hubei, Huangshi
HS Code
7228600000
Production Capacity
500tons Per Month
Reference Price
$ 450.00 - 4,500.00
Contact Us

Product Description

packaging & delivery
packing details: in seaworthy packing,as your requirement.
delivery details: within 30-50days.
 
shape: round, square, flat
 
Features:

2.immediate delivery
3.premium quality
4.reliable service


1.2063 STEEL Suitability

1.2063 Steel suitable for cutting tools, profile knives and milling machines for a fine machining of coloured metals and plastics by lower cutting speeds, machine files, tools for woodworking, tools for cold cutting, circular cutting knives.

 Chemical composition:

C Mn Si P S Cr Ni Mo W V Cu
1.3-1.45 0.4-0.7 0.15-0.4 0.03max 0.03max 1.3-1.65 0.35max 0.2max 0.2max 0.1-0.25 0.35max
 
Way Temperature [°C] Procedure
Forging 850-1050 Cool slowly in calm air or better e.g. in dry ash.
Soft annealing 750-780 Nkolik hodin prohát (podle velikosti pedmtu), vt?inou staí 4 hodiny a pomalu ochlazovat v peci. Warm few hours (according to the size of object), mostly four hours are enough and cool slowly in the furnace.
Annealing to lower tension 600-650 Warm 1 to 2 hours and cool slowly in the furnace.
Hardening in oil 830-870 Cool in air, the degree of tempering is set by hardness and toughness of instrument according to the tempering chart.
Tempering 150-250 Cool in air.

Note
Chart of tempering values depending on the hardness:
°C 100 200 300 400
HRC 64 63 60 56
 
1.2063 Value
Technological treatment processes
Hardness after hardening HRC (HRC) >=62
Hardness after soft annealing HB (HB) <=248
Hardness after hardening and tempering 150 ° C HRC (HRC) >=62
Hardness after hardening and tempering 200 ° C HRC (HRC) >=62
Hardness after hardening and tempering 250 ° C HRC (HRC) 60,3
Hardness after hardening and tempering 300° C HRC (HRC) 58
Hardness after hardening and tempering 350° C HRC (HRC) 55
Hardness after hardening and tempering 400° C HRC (HRC) 52
Hardness after hardening and tempering 450° C HRC (HRC) 48,6
Hardness after hardening and tempering 500° C HRC (HRC) 45


Steel grades according to PN (Polish Standards) and W.No. as well as their equivalents
PN W.No. DIN EN AISI RUSSIA CHINA BÖHLER
NC6 1.2063 1.2063 - - - - -

 
Cold Work 1.2063 Steel (DIN1.2063) Cold Work 1.2063 Steel (DIN1.2063) Cold Work 1.2063 Steel (DIN1.2063) Cold Work 1.2063 Steel (DIN1.2063)