Cpm4V Material Powder Metallurgy Tool Steel Black Surface Forging Steel Hot Rolled Steel Flat Bar Round Bar
Model NO.
powder tool steel
Composition
Stainless Steel Scrap
Technique
Forged
Shape
Bar
Surface Treatment
Polished
Special Use
High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
Application
Die Steel Bar
Length
2500-5500mm
Material
HSS
Usage
Gear Hob
Customized Support
OEM
Transport Package
N/M
Specification
6-400mm
Trademark
Smooth
Origin
China
HS Code
7226911000
Production Capacity
1000ton/Month
Reference Price
$ 37,260.00 - 41,400.00
Description
Product Description
Typical Composition
:
CPM 4V is a powder metal tool steel with an outstanding combination of properties including high impact toughness and very good wear resistance. CPM 4V should be considered for service in fine blanking, powder compaction tools, for processing high-strength low-alloy (HSLA) steels, advanced high-strength steels (AHSS) and applications where a combination of strength , wear resistance and toughness is required. CPM 4V should be considered for applications where a higher attainable hardness and additional abrasion resistance is required than can be offered by CPM 3V.
Chemical Composition:
Physical Properties
Density: 0.278 lb/in3 (7700 kg/m3)
Specific Heat: 0.11 Btu/lb/ºF (460 J/kg°C)
Modulus of Elasticity: 30x106 psi (207 GPa)
Machinability: 50-60% of a 1% carbon steel
HEAT TREATING INSTRUCTIONS
HARDENING:
Preheating: 1500-1550°F (816-845°C), equalize.
Austenitizing (High Heat): Heat rapidly from the preheat.
For Maximum Wear Resistance:
Furnace or Salt Bath: 2100°F (1149°C) Soak for 15 minutes at temperature
For Balanced Wear & Toughness:
Furnace or Salt Bath: 1875-1950°F (1024-1065°C) Soak for 30 minutes at temperature
For Maximum Toughness:
Furnace or Salt Bath: 1800°F (982°C) Soak for 30 minutes at temperature
Quenching:
Air, pressurized gas, warm oil, or salt. For pressurized gas, the furnace should have a minimum quench pressure of 4 bars. For oil, quench until black, about 900°F (482°C), then cool in still air to 150-125°F (66-51°C). For salt maintained at 1000-1100°F (538-593°C), equalize in the salt, then cool in still air to 150 125°F (66-51°C).
Tempering:
Temper immediately after quenching. Typical temperature range is 1000-1100°F (538 593°C). Do not temper below 1000°F (538°C). Hold at temperature for 1 hour per inch of thickness, 2 hours minimum, then air cool to ambient temperature. Double tempering is required.
ANNEALING:
Annealing must be performed after hot working and before rehardening. Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1600-1650°F (871-899°C), and hold at temperature for 1 hour per inch of maximum thickness; 2 hours minimum. Then cool slowly with the furnace at a rate not exceeding 50°F per hour (28°C per hour) to 1000°F (649°C). Continue cooling to ambient temperature in the furnace or in air.
The resultant hardness should be approximately 241 HBW.
CPM 4V is a powder metal tool steel with an outstanding combination of properties including high impact toughness and very good wear resistance. CPM 4V should be considered for service in fine blanking, powder compaction tools, for processing high-strength low-alloy (HSLA) steels, advanced high-strength steels (AHSS) and applications where a combination of strength , wear resistance and toughness is required. CPM 4V should be considered for applications where a higher attainable hardness and additional abrasion resistance is required than can be offered by CPM 3V.
Chemical Composition:
| CPM 4V | C | Mn | Si | Cr | Mo | V |
| 1.35 | 0.40 | 0.80 | 5.00 | 2.95 | 3.85 |
Physical Properties
Density: 0.278 lb/in3 (7700 kg/m3)
Specific Heat: 0.11 Btu/lb/ºF (460 J/kg°C)
Modulus of Elasticity: 30x106 psi (207 GPa)
Machinability: 50-60% of a 1% carbon steel
HEAT TREATING INSTRUCTIONS
HARDENING:
Preheating: 1500-1550°F (816-845°C), equalize.
Austenitizing (High Heat): Heat rapidly from the preheat.
For Maximum Wear Resistance:
Furnace or Salt Bath: 2100°F (1149°C) Soak for 15 minutes at temperature
For Balanced Wear & Toughness:
Furnace or Salt Bath: 1875-1950°F (1024-1065°C) Soak for 30 minutes at temperature
For Maximum Toughness:
Furnace or Salt Bath: 1800°F (982°C) Soak for 30 minutes at temperature
Quenching:
Air, pressurized gas, warm oil, or salt. For pressurized gas, the furnace should have a minimum quench pressure of 4 bars. For oil, quench until black, about 900°F (482°C), then cool in still air to 150-125°F (66-51°C). For salt maintained at 1000-1100°F (538-593°C), equalize in the salt, then cool in still air to 150 125°F (66-51°C).
Tempering:
Temper immediately after quenching. Typical temperature range is 1000-1100°F (538 593°C). Do not temper below 1000°F (538°C). Hold at temperature for 1 hour per inch of thickness, 2 hours minimum, then air cool to ambient temperature. Double tempering is required.
ANNEALING:
Annealing must be performed after hot working and before rehardening. Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1600-1650°F (871-899°C), and hold at temperature for 1 hour per inch of maximum thickness; 2 hours minimum. Then cool slowly with the furnace at a rate not exceeding 50°F per hour (28°C per hour) to 1000°F (649°C). Continue cooling to ambient temperature in the furnace or in air.
The resultant hardness should be approximately 241 HBW.
Alloy Steel
-
ASTM B127-1998 ASTM B162-1999 Nickel Plating Line Plate Sheet Hastelloy C276 Nickel Cathodes for Electroplating
X21h28b5m3Б Ap Alloy э Π 126 Plate BЖ 100 Price
Cold Drawn Carbon Steel Profile for Steel Body Sliding Contact Line of Crane
High Standard ASTM4047 ASTM4118 ASTM4120 ASTM4121 Free Cutting Steel Alloy Steel Plate Sheet with Superior Wear Resistance
Smooth AISI 1020 Carbon Steel Round Flat Plate Sheet Bar Origin China
Nai-Lok N06625 ASTM B444 Alloy 625 Nickel Alloy Seamless Tube B829 Alloy 625 690 DIN2.4856 Bright Annealed Solution Molybdenum Nickle Alloy Steel Pipe/Tube
Food Grade 304 Stainless Steel Pipes From China
Stock All Series Stainless Steel Tubes for Sale From China
AISI 94b17 80-650mm Forged Quenched Polished Alloy Steel
Smooth AISI 1020 Carbon Steel Round Flat Plate Sheet Bar Specification
AISI 50b60 80-650mm Forged Quenched Polished Alloy Steel
High Temperature Alloy GH1131 /GH131 Alloy Plate Factory Price OEM/ODM
Nai-Lok Alloy 400 Seamless Steel Pipe Tubing 1/8' Od Bright Annealed (BA) Finish ASTM B165 for Instrumentation & Fluid Control Systems
S45c/C45/1045 Cold Drawn Round Steel for Linear Bearing Shaft
Alloy Steel Pipe Tube Astme9310 50b44 50b46 50b50 50b60 51b60 81b45 94b17 94b30 Customized Carbon Steel Pipe Seamless Round Pipe
AISI 50b50 80-650mm Forged Quenched Polished Alloy Steel