AISI3415 AMS6260e 655h13 15nicr13 1.5752 Case Hardening Steel

Model NO.
AISI3415 AMS6260E 655H13 15NiCr13 1.5752
Composition
Ferrous Steel Scrap
Technique
Hot Forged or Hot Rolled
Shape
Round, Flat or Square
Surface Treatment
Black Surface, Grinded, Peeled, Milled, Polished
Special Use
Alloy Structural Steel
Application
Structural Steel Bar
Size Range
Round Bar:Dia12~420mm Flat Bar:2~420 X 30~1500mm
Smelting Process
Ef, Eaf, ESR
Delivery Condition
Hot Rolled, Forged, Annealed, Quenched and Tempered
Surface Condition
Black Surface, Grinded, Peeled, Milled, Polished
Transport Package
Seaworth Packing
Specification
Round Bar: Dia12~420mm Flat Bar: 2~420 X 30~1500mm
Trademark
CHENGQUAN
Origin
Huangshi, Hubei
HS Code
7228100000
Production Capacity
5000tons/Year
Reference Price
$ 450.00 - 4,500.00
Contact Us

Product Description

AISI3415 AMS6260e 655h13 15nicr13 1.5752 Case Hardening Steel AISI3415 AMS6260e 655h13 15nicr13 1.5752 Case Hardening Steel AISI3415 AMS6260e 655h13 15nicr13 1.5752 Case Hardening Steel AISI3415 AMS6260e 655h13 15nicr13 1.5752 Case Hardening Steel Description

15NiCr13 is a remelted nickel chrome molybdenum case hardening steel produced by the PESR* (Pressurised ESR) method designed for components with high demand in toughness and core strength.

Application

Highly stressed components in automotive construction, and for general engineering purposes, e. g. gears, crankshafts, gearshafts.

Advantages

Good machinability (hobbing and turning).
Good dimensional stability.
Homogenous PESR structure suitable for the production of large components.
Improved polishability, photo-etchability and EDM due to higher purity.
Suitable for single and double hardening.

All Grades Comparison

DIN EN ANFOR BS GOST AISI AMS UNI
1.5752 15NiCr13 14NC11 655H13 G55M13 3415 6260E 18NC13

Quality Standard

BS EN 10084 2008 Case hardening steels - Technical delivery conditions
BS EN 10277-4-2008 Bright steel products -Case Hardening Steel- Part 4 General

Chemical Composition(%)

C Mn Si P S Cr Ni
0.14-0.20 0.40-0.70 0.40 max 0.025 max 0.035 max 0.60-0.90 3.00-3.50

Mechanical Properties(T=20°C if not differently stated)

Process Diameter(mm) Tensile Strength Rm (Mpa) Yield Strength Rp0.2 (Mpa) Elongation A5 (%) Area Reduction Ratio C (%) Hardness (HB)
SOFT ANNEALED / / / / / 255 max
Treated to hardness range / / / / / 179-229
Treated to ferrite-pearlite structure / / / / 166-217  
QUENCHED AND TEMPERED 11 max 1030-1320 835 min 9 min 40 min /
QUENCHED AND TEMPERED 11-30 930-1230 785 min 10 min 45 min /
QUENCHED AND TEMPERED 30-63 880-1180 735 min 10 min 45 min /

HEAT TREATMENT:

Process Temperature(°C)
End quench test Austenitizing 880 min
Carburizing 880-980
Core-hardening 840-880
Case-hardening 780-820
Tempering 150-200 /

Mill′s test certificate:

EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.
 