1.7131 16hg 16mncr5 Factory Price Special Alloy Spring Steel Rod Round Bar

Model NO.
Round bar
Composition
Ferrous Steel Scrap
Technique
Forged
Shape
Bar
Surface Treatment
Machined
Special Use
High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel, Die Material
Application
Tool Steel Bar
Length
2500-5500mm
Transport Package
N/M
Specification
6-400mm
Trademark
Smooth
Origin
China
HS Code
7228400000
Production Capacity
5000ton/Month
Reference Price
$ 540.00 - 1,350.00
Contact Us

Product Description

APPLICATION:

Alloyed case hardening steel for parts which require high core tensil strength and high hardness. Susceptible to the small seized parts with medium wearing resistance and average loading such as: gears, screws, bolts, bushing and camshafts.

TECHNOLOGICAL INFORMATION:

Steel adjusted for cutting with a cutting machine. The carburising temperature range can be higher than provided in the file (depending on the carburising process)

SEMI-FINISHED PRODUCTS:

Steel adjusted for cutting with a cutting machine. The carburising temperature range can be higher than provided in the file (depending on the carburising process)

CHEMICAL COMPOSITION:

C Si Mn P S Cr Mo Ni B
0,14-0,19 Max 0,40 1,00-1,30 Max 0,025 Max 0,035 0,80 - 1,10 - - -

MECHANICAL PROPERTIES:

Hardness after: Symbol Value
Soft annealing (+A) HB ≤ 207
Heat treatment (carburising, quenching and tempering) (+QT) HRC ≥ 60
Ultimate tensile strength R m , after quenching and tempering at 200 °C:
Diameter, d, mm d ≤ 16 16 < d ≤ 40 40 < d ≤ 100
R m , MPa 970 820 620

PHYSICAL PROPERTIES:

Property Unit Value
Density, ρ g·cm -3 7.85

HARDENABILITY:

EN10084:2008

Jominity test HRC mm (mm distance from quenched end)

1,5 3 5 7 9 11 13 15 20 25 30 35 40
max. 47 46 44 41 39 37 35 33 31 30 29 28 27
min. 39 36 31 28 24 21 - - - - - - -

TECHNOLOGICAL TREATMENT PROCESSES:

Technological treatment processes Possible application Temperature, °C
Hot forming Forging + 1150 - 850
Rolling + 1150 - 850
Thermochemical treatment Carburising + 880 - 980
Carbonitriding + 860 - 950
Heat treatment Annealing Normalising + 870 - 910
Soft annealing + 650 - 700
Heat treatment after carburising 1) Core hardening + 860 - 900
Intermediate annealing + 670 - 720
Case hardening + 780 - 820
Tempering + 150-200
1)   If possible, hardening has to be performed with the temperature equal or close to the heat treatment temperature

INTERNATIONAL STEEL GRADES:

ISO CEN Russia
16MnCr5 ISO 683-11:1987 16MnCr5 EN 10084:1998 ~18HG GOST 4543-71
US Japan China
~5115 ASTM A 29-99 - - ~15CrMn GB 3077-88
 
1.7131 16hg 16mncr5 Factory Price Special Alloy Spring Steel Rod Round Bar 1.7131 16hg 16mncr5 Factory Price Special Alloy Spring Steel Rod Round Bar 1.7131 16hg 16mncr5 Factory Price Special Alloy Spring Steel Rod Round Bar 1.7131 16hg 16mncr5 Factory Price Special Alloy Spring Steel Rod Round Bar 1.7131 16hg 16mncr5 Factory Price Special Alloy Spring Steel Rod Round Bar 1.7131 16hg 16mncr5 Factory Price Special Alloy Spring Steel Rod Round Bar 1.7131 16hg 16mncr5 Factory Price Special Alloy Spring Steel Rod Round Bar 1.7131 16hg 16mncr5 Factory Price Special Alloy Spring Steel Rod Round Bar

 

1.7131 16hg 16mncr5 Factory Price Special Alloy Spring Steel Rod Round Bar
1.7131 16hg 16mncr5 Factory Price Special Alloy Spring Steel Rod Round Bar

Leave Your Message

 

Alloy Steel
✉ Contact Supplier