High Alumina Anchoring Brick for Kiln Roof

Model NO.
YUFENGREC -A55
Size(Shapes)
Straights, Arch, Wedge, Soaps, Splits...
Bulk Density
2500 Kg/M3
Type
Refractory Material
Material
Pure Bauxite
Transport Package
Export Standar Wooden Pallet
Specification
ASTM Standard
Trademark
YUFENGREC
Origin
China
HS Code
69022000
Production Capacity
30000 Tons /Year
Reference Price
$ 144.00 - 529.20
Contact Us

Product Description

High Alumina Anchoring Brick for Kiln Roof
YUFENGREC ®   High Alumina Anchor Brick   are made of  Pure  Bauxite  ,  with alumina content from 55% to 85% , producing by drying pressing and high fired .
 

Classification : ASTM C-27

 

Method of Manufacturer: Dry Pressing


Key Features 

* High Strength

* Lower Shrinkage

* Excellent Alkalis Resistant
* Good resistant to Thermal Shock

* High Refractoriness under load

Typical Applications

* Carbon Baking pit furnace   flue-walls and head walls

* Air Heaters

* Combustion Chamber .

* Boiler

* Stack

* Blast Furnace

* Hot Blast Stove

* Cement Rotary Kiln

* Glass Furnace

* kinds of high temperature   industry furnace

 

Dimensions

 

Packing   

* In export standard wooden pallet

Typical Technical Data

* High Alumina Brick  

Item High Alumina Brick 
SK36 SK37  SK38 SK40
Al 2 O 3   55% 60 70 79.6
Fe 2 O 3   2.0% 2.0% 2.0% 2.0%
Pyrometric Cone Equivalent           Orton Standard Cones  35 37 38 40

Bulk Density 		2.30 g/cm3 2.35g/cm3 2.45 g/cm3 2.60 g/cm3

Cold crushing strength 		31 MPA 44 MPA 48 MPA 55 MPA

Apparent Porosity 		22% 22% 21% 20%

Permanent Linear Change at 1600 ºC 		+0.1 to +2.5%  +1.5 to +2.5%  +2.0 to +4.0%  +1.0 to +2.0% 



Producing Procedure 
High Alumina Anchoring Brick for Kiln Roof
QC Inspection
High Alumina Anchoring Brick for Kiln Roof High Alumina Anchoring Brick for Kiln Roof
High Alumina Anchoring Brick for Kiln Roof
Applications 
ZIBO YUFENG REFRACTORY CO,LIMITED products are widely used
and can be applied to multiple scenes.  
High Alumina Anchoring Brick for Kiln Roof


 

Leave Your Message

 

Alumina Refractory Material
✉ Contact Supplier